advanced glass/mineral filled PPS compound.
|
Property |
Test Method |
Units |
Fiberglass/Mineral Reinforced |
|
P250T |
P260T |
P260W |
P265T |
P265U |
|
Physical |
Density |
ISO 1183 |
g/cm3 |
1.74 |
1.90 |
1.96 |
1.98 |
1.92 |
|
Water Absorption |
ISO 62 |
% |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
|
MD/TD* |
- |
% |
0.3/0.5 |
0.2/0.4 |
0.2/0.4 |
0.2/0.4 |
0.3/0.4 |
|
Mechanical |
Tensile Strength |
ISO 527 |
MPa |
160 |
150 |
170 |
140 |
100 |
|
Elongation at Break |
ISO 527 |
% |
3.0 |
2.0 |
2.0 |
2.0 |
1.0 |
|
Flexural Strength |
ISO 178 |
MPa |
220 |
200 |
245 |
200 |
150 |
|
Flexural Modulus |
ISO 178 |
GPa |
12.0 |
18.0 |
18.0 |
18.0 |
16.0 |
|
Impact Strength |
ISO 180 |
kJ/m2 |
10.0 |
9.0 |
10.0 |
7.5 |
5.0 |
|
Rockwell Hardness |
ISO 2039/2 |
R scale |
120 |
120 |
120 |
120 |
120 |
|
Thermal |
Heat Deflection Temperature |
ISO 75 |
¡æ |
265 |
265 |
265 |
265 |
265 |
|
Flammability Rating |
UL-94 |
- |
V0 |
V0 |
V0 |
V0 |
V0 |
|
Electrical |
Volume Resistivity |
ISO 167 |
Ohm.cm |
5¡Á1016 |
5¡Á1016 |
5¡Á1016 |
5¡Á1016 |
5¡Á1016 |
|
Dielectric Strength |
ASTM D149 |
KV/mm |
16 |
16 |
16 |
16 |
16 |
|
Dielectric Constant |
ASTM D150 |
- |
4.2 |
4.2 |
4.2 |
4.2 |
4.2 |
|
Wastage Factor |
ASTM D150 |
- |
0.002 |
0.002 |
0.002 |
0.002 |
0.002 |
|
Process
Conditions |
Injection Temperature |
- |
¡æ |
290¡«330 |
290¡«330 |
290¡«330 |
290¡«330 |
290¡«330 |
|
Mold Temperature |
- |
¡æ |
120¡«150 |
120¡«150 |
120¡«150 |
120¡«150 |
120¡«150 |
|
* MD: Mold direction; TD: Transverse direction |
Available Color: Black and Nature Color